ANALISIS KEAUSAN & KOEFESIEN GESEK MATERIAL BAJA AISI 1045 COATING MENGGUNAKAN TRIBOMETER PIN ON DISC

Authors

  • Irwan Ardiyatna susi Fakultas Teknik dan Informatika, Progam Studi Teknik Mesin Universitas PGRI Semarang
  • Althesa Androva Dosen Teknik Mesin, Fakultas Teknik dan Informatika Universitas PGRI Semarang
  • Aan Burhanuddin Dosen Teknik Mesin, Fakultas Teknik dan Informatika Universitas PGRI Semarang

Keywords:

wear, coating variations, pin-on-disc

Abstract

Pin-on-disc is a tool component of a tribometer that is used to test or determine the wear and friction values of a material object. Pin-on-disc consists of a ball-shaped pin and a disc-shaped disc made of steel (Prabowo et al, 2012). The research aims to determine the comparison of wear and friction levels of AISI C1045 steel material using a variety of coatings, namely without coating, half coating, one layer of coating, and 2 layers of coating. The highest wear value lies in the 2nd layer coating variation with a wear value of 59.985 gr/s.mm2. while the lowest wear value lies in the variation of without coating, namely -19.13 gr/smm2. Meanwhile, in the friction coefficient comparison, the highest value occurred in the one layer coating variation, namely 0.46, and the lowest geek coefficient value occurred in the 2 layer coating test, namely -0.481. The conclusion from these results is that variations in coating thickness will affect the wear rate of the disc material. It can be seen from the data that has been obtained that the 2 layer coating variation has a very high wear value compared to other variations.

References

Arifin, J., Purwanto, H., & Syafa’at, I. (2017). Pengaruh Jenis Elektroda Terhadap Sifat Mekanik Hasil Pengelasan. Momentum, 13(1), 27–31.

Prabowo, D., Burhanudin, A., Armanto, E., Dwi, D. K., JAMARI, & SYAIFUL. (2012). RANCANG BANGUN DAN PENGUJIAN PEMANAS PADA DISC UNTUK ALAT UJI TRIBOMETER TIPE PIN-ON- DISC.

Pramono, A. (2011). Karakterisrik Mekanik Proses Hardening Baja Aisi 1045 Media Quenching Untuk Aplikasi Sprochet Rantai. In Jurnal Ilmiah Teknik Mesin (Vol. 5, Issue 1). www.uddeholm.com,

Rachman, Y. M., Maulana, A., & Ekawati, F. D. (2020). Pengaruh Proses Hardening Baja Aisi 1045 Terhadap Sifat Keausan. Jurnal Ilmiah Teknik Mesin, 8(2), 89–95. https://doi.org/10.33558/jitm.v8i2.2187

Syafa’at, I., Jamari, Widyanto, S. ., & Ismail, R. (2010). Pemodelan Keausan Kontak Sliding Antara Slinder Dengan Bidang Datar. Junal.Unimus.Ac.Id, 024.

Downloads

Published

2024-05-21 — Updated on 2024-08-22

Versions

Issue

Vol. 2 No. 6 (2024): Juni

Section

Articles